Abstract
The X and U phases of hexagonal ferrites are notoriously difficult to make as pure materials, and what little data there is published regarding their physical or magnetic properties relates only to single crystals. Stoichiometric Co2X and Co2U fibres were made from a sol-gel based process, and the characteristics of the sols and fibres were studied using PCS, XRD, SEM and VSM. The evolution of the X and U fibres was studied, and shown to be similar that of the W and Z fibres whose structures they respectively resemble. Co2X and Co2U had been formed at 1200°C, and the morphology of the fibres was different from those of the W and Z phases. The magnetic properties, again while resembling the W and Z phases, were different to any of the other hexagonal ferrite fibres. The magnetic hysteresis loops of both fibres were magnetically as was, the Co2X fibres having M s = 45.0 emu g−1 and H c = 0.085 T, and the Co2U fibres having M s = 51.5 emu g−1 and H c = 0.059 T.
Similar content being viewed by others
References
G. H. Jonker, H. P. J. Wijn and P. B. Braun, Phil. Tech.Rev. 18 (1956) 145.
J. Smit and H. P. J. Wijn, “Ferrites” (Philips Technical Library, Eindhoven, 1959).
G. A. Jones, S. F. H. Parker, J. G. Booth and D. S. Simkin, IEEE Trans.Mag. MAGN-26 (1990) 2804.
A. Tauber, J. S. Megill and J. R. Shappirio, J.Appl. Phys. 41 (1970) 1353.
J. A. Kohn, D. W. Eckart and C. F. Cook Jr., Science 172(3983) (1971) 519.
A. J. Kerecman, A. Tauber, T. R. Avlon and R. O. Savage, J.Appl.Phys. 39 (1968) 726.
R. C. Pullar, S. G. Appleton and A. K. Bhattacharya, J.Magn.Mag.Mat. 186 (1998) 326.
R. C. Pullar, M. D. Taylor and A. K. Bhattacharya, J.Mater.Sci. 32 (1997) 365.
Idem., ibid. 32 (1997) 873.
R. C. Pullar, S. G. Appleton, M. H. Stacey, M. D. Taylor and A. K. Bhattacharya, J.Magn.Mag.Mat. 186 (1998) 313.
M. J. Morton, J. D. Birchall and J. E. Cassidy, UK Patent no. 1360197 (July 1974).
C. Suryanarayana and M. Grant norman, “X-Ray Diffraction—A Practical Approach” (Plenum Press, New York, 1998) p. 212.
R. C. Pullar, M. H. Stacey, M. D. Taylor and A. K. Bhattacharya, Acta Mat., submitted.
R. C. Pullar and A. K. Bhattacharya, J.Magn.Mag. Mat., submitted.
Idem., J.Phys.D, submitted.
Idem., J.Magn.Mag.Mat., submitted.
R. C. Pullar, unpublished work.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pullar, R.C., Bhattacharya, A.K. The synthesis and characterisation of Co2X (Ba2Co2Fe28O46) and Co2U (Ba4Co2Fe36O60) ferrite fibres, manufactured from a sol-gel process. Journal of Materials Science 36, 4805–4812 (2001). https://doi.org/10.1023/A:1017947625940
Issue Date:
DOI: https://doi.org/10.1023/A:1017947625940