High performance cork-templated ceria for solar thermochemical hydrogen production via two-step water-splitting cycles

Abstract

Water splitting by solar energy-driven two-step thermochemical cycles is a promising approach for large-scale production of renewable fuels (e.g. hydrogen). The key challenge is developing materials capable of withstanding the harsh environmental conditions and to ensure high reliability in use, particularly in terms of redox kinetics and better activity at low operation temperatures. In this work, we demonstrate that cork-templated ceria can significantly enhance the hydrogen production performance under solar irradiation heating. Three types of ceria morphologies were synthesised and investigated in two-step thermochemical redox cycles, namely ceria granules (ecoceramics) prepared from cork templates based on either a green water-based or an acetone solvent-based approach, as well as ceria foams replicated from polyurethane templates. These materials were cycled in a high-temperature indirectly-irradiated solar tubular reactor, heated via concentrated solar light, using a temperature-swing process. Samples were typically thermally reduced at 1400–1450 °C and subsequently re-oxidised with H2O between 950–1150 °C. The green synthesis ceria granules had up to 25% and 32% higher average H2 production yields than the acetone-based ecoceramics and replicated ceria foams, respectively. On average, H2 production rates for cork-templated ceria granules (1.3 ± 0.2 mL min−1 g−1) were up to ∼60% higher than for ceria foams (0.8 ± 0.3 mL min−1 g−1), indicating that the morphology of this three-dimensionally ordered macroporous (3-DOM) CeO2 improves the reaction kinetics. This is attributed to the smaller mean cell size of the cork-derived ecoceramic (25 μm) compared to that of the replicated ceria foam (575 μm), suggesting that their semi-closed wall cells enhanced reaction rates. The increase in reduction temperature from 1400 to 1450 °C resulted in the highest H2 production rate (1.6 mL min−1 g−1) reported so far for 3-DOM ceria. Neither loss in redox performance nor change in grain morphology was observed from the first to the last cycle. These findings show that cork-like structural features are key to engineering efficient materials for enhanced solar thermochemical fuel production.

Graphical abstract: High performance cork-templated ceria for solar thermochemical hydrogen production via two-step water-splitting cycles

Article information

Article type
Paper
Submitted
27 Feb 2020
Accepted
17 Apr 2020
First published
17 Apr 2020

Sustainable Energy Fuels, 2020,4, 3077-3089

High performance cork-templated ceria for solar thermochemical hydrogen production via two-step water-splitting cycles

F. A. Costa Oliveira, M. A. Barreiros, A. Haeussler, A. P. F. Caetano, A. I. Mouquinho, P. M. Oliveira e Silva, R. M. Novais, R. C. Pullar and S. Abanades, Sustainable Energy Fuels, 2020, 4, 3077 DOI: 10.1039/D0SE00318B

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements