Production of rGO-Based Electrospinning Nanocomposites Incorporated in Recycled PET as an Alternative Dry Electrode
Next Article in Special Issue
Exploring the Materials and Condition of 20th-Century Dolls in Zoe Leonard’s Mouth Open, Teeth Showing 2000
Previous Article in Journal
Advances in the Measurement of Polymeric Colorimetric Sensors Using Portable Instrumentation: Testing the Light Influence
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Mattel’s Barbie: Investigation of a Symbol—Analysis of Polymeric Matrices and Degradation Phenomena for Sixteen Dolls from 1959 to 1976

1
YOCOCU, Youth in Conservation of Cultural Heritage, Via T. Tasso 108, 00185 Rome, Italy
2
Department of Biology, Ecology and Earth Sciences DIBEST, University of Calabria, Via Pietro Bucci, Arcavacata, 87036 Rende, Italy
3
Department of Earth Sciences, Sapienza University of Rome, Piazzale Aldo Moro 5, 00185 Rome, Italy
4
Department of Environmental Biology, Sapienza University of Rome, Piazzale Aldo Moro 5, 00185 Rome, Italy
5
Interventi Conservativi Storico Artistici (ICSA s.r.l.), Via Oriano Sotto 2/A, 21018 Sesto Calende, Italy
6
Department of Environmental Sciences, Informatics and Statistics, Ca’ Foscari University of Venice, Via Torino 155, 30170 Venezia Mestre, Italy
*
Author to whom correspondence should be addressed.
These authors contributed equally to this work.
Polymers 2022, 14(20), 4287; https://doi.org/10.3390/polym14204287
Submission received: 12 September 2022 / Revised: 21 September 2022 / Accepted: 6 October 2022 / Published: 12 October 2022
(This article belongs to the Special Issue Polymeric Materials in Modern—Contemporary Art II)

Abstract

:
Mattel’s Barbie dolls are the most famous and iconic dolls since 1959. Today, they are being collected by individuals and often conserved in museum environments due to their cultural and historical significance reflecting everyday life and historical events. However, just like most museum objects made of plastics, both historical and more recent Barbies show evident degradation phenomena. Firstly, Barbies were made of plasticized polyvinyl chloride (PVC), affected by the migration of additives—mostly the plasticizers—from the bulk phase to the outermost layer, appearing as a tacky and glossy exudate. Over the years, Barbies’ polymeric constituents were replaced with more stable ones, whose additives migration is limited compared to PVC, even though still occurring. Multispectral photography in visible (VIS) and ultraviolet (UV) light, microscopical observations in VIS and UV light, and Fourier Transform Infrared spectroscopy in the Attenuated Total Reflectance mode (FT-IR ATR) were performed to characterize the constituent materials of 15 Barbies produced between 1959 and 1976, bridging the information gap on their processing over the years. The micro-invasive multi-analytical approach also allowed for the characterization of the degradation products, permitting the reference of the exudated compound to the specific bulk polymer.

1. Introduction

Plastics entered the technological scene at the beginning of the 20th century. During the past decades, artists, designers, and architects have used these synthetic materials to create pieces that are now recognized as iconic items. Hence, they have become a significant part of many museum collections, posing major problems for collectors and conservators, due to their fast degradation [1]. Plastic items have defined our culture: ordinary objects, such as toys, are the reflection of significant social developments in political, cultural, scientific, and military history [2,3]. Children’s toys are part of social memory, mirroring the needs of the period when they were produced. It is possible to obtain information on the toy trade and understand the aspects of perception and use of historical culture [4].
Few toys have impacted fashion, style, and culture as intensely as Mattel’s Barbie doll, which was first produced in 1959 [5]. She is the best-selling and most famous doll ever [6]. Barbie has been the most iconic toy since the early 60s and continues to be very popular even today. It emphasized the importance of the female gender in society long before many living women had such opportunities [7]. Barbie was represented as a businesswoman as well as holding the usual gender roles for the 1960s [8]. Numerous versions of Barbie include various roles that a woman from the 1960s to the 1990s could hardly hope for, such as professor, librarian, nurse, vet, astronaut, NASCAR driver, babysitter, and presidential candidate [9]. This amazing fusion between Barbie and the community pushed the interest of museums in the preservation of Barbies [10].
From a material point of view, Barbies are plastic artifacts, prone to fast deterioration, and their conservation may represent a challenge as well as an opportunity for collectors and museum conservators. From a technological point of view, plastics are characterized by virtually endless possibilities for formulation of different polymers, with different characteristics [2,11]. Chemical-physical properties of polymers also depend on the presence of different additives, which are known to affect both the long-term stability and an object’s appearance during the degradation process [10,11,12]. One of the major problems associated with the applications of polymers is their instability in weathering and daylight [13,14]. It is well known that UV light and the short wavelengths of visible light (VIS) can induce photochemical processes in organic polymers, which result in dramatic changes in the polymeric matrix. The degradation phenomena can be measured in years, which is considerably less than that of traditional art and heritage materials, often measured in hundreds or thousands of years. Understanding the mechanisms of the reactions that produce degradation of polymer properties has thus been the subject of intensive research over the past 50 years [1,13,15,16,17,18]. In most cases, the main cause of deterioration is photooxidation, which is initiated by light irradiation [19]. Radiation in the ultraviolet and visible is indeed the primary factor in polymer weathering. Effects from heat, moisture, pollutants, mechanical stresses, and biological attacks also play a role, but in many cases, the weathering process begins with a photochemical event. Solar UV light induces photochemical processes in organic materials, which result in the fixation of oxygen, rearrangements, chain scissions, cross-linking, photo-discoloration, and photo-bleaching. All these processes contribute to a decrease in the various properties of the materials, such as optical, mechanical, and electrochemical properties [20].
Despite the very large effort put into the development of mechanical and chemical methods for assessing degradation, the links between chemical reactions and engineering failure in weathered polymers are far from being completely elucidated. In addition to sociological factors, an analysis of the evolution of Barbie dolls may include an assessment of their technological production, which can maintain industrial historical memory. Indeed, the Mattel doll underwent about 50,000 structural and design changes since its first release based on users’ needs and social changes [8,9,21]. Since the first Barbie, produced in 1959 using plasticized polyvinyl chloride (PVC), the constituent materials of Barbies have changed over time also because the bulk polymer was not stable enough, causing premature whitening due to the reaction of vinyl-based polymers with light [22]. The recipe of the polymer matrix changed both due to degradation problems and also because of economic and legal constraints of the specific production period [23].
To better understand the effect of these technological modifications, 15 Barbies produced between 1959 and 1976, based on the year reported on the Barbie itself, have been studied. The first aim of this study was to evaluate the Barbies’ constituent materials to bridge the information gap regarding the evolution of the most famous doll manufacturing process. Only a few data on Barbies’ processing changes over the years are available so far, making the selection of the most appropriate preservation strategy even more challenging [5,23]. Besides, each of them is characterized by different deterioration phenomena, mainly consisting of the formation of a glossy or crystal-like white patina on the surface which gives rise to dust embedding and color alteration over time. An effort has been made to relate constituent materials to specific degradation products using a micro-invasive analytical approach, permitting identification of compounds that tend to migrate to the surface layer. At the same time, the appearance of the different exudates was examined to attempt a prediction of their composition based on visual features.

2. Materials and Methods

Fifteen Barbie dolls have been analyzed. Their dating is as follows:
  • 1959/1960: Barbies #1 and 2.
  • 1964: Barbies #3 to 6.
  • 1965: Barbies #7 and 8.
  • 1972: Barbies #9 and 10.
  • 1974/1976: Barbies #11 to 15.
The Barbies’ general conditions were examined through macroscopic and microscopic inspection. Multispectral photography was carried out using a multispectral system (Madatec, Milan – Italy), consisting of a Digital Camera (Samsung NX500—28.2 MP BSI CMOS) and Madatec spotlights with 365 nm wavelength (UV light). Images of the induced fluorescence were taken using the HOYA UV-IR filter cut 52 (Kenko Tokina Co. Ltd., Tokyu – Japan) [24,25,26]. An optical portable microscope Dino-Lite AM411-FVW (Dino-Lite Europe, Almere – Netherlands) was used at different magnifications—from 40× to 220×—and illumination modes—visible light (VIS), ranking light (VIS-RAD), and ultraviolet light (UV) to better evaluate the deterioration phenomena on the surface of the polymeric matrix. The acquired images enabled the selection of the most significant areas for the subsequent analysis performed using Fourier Transform Infrared spectroscopy in the Attenuated Total Reflectance mode (FT-IR ATR). Most of the FT-IR ATR analysis was carried out by directly placing each element comprising the dolls on the diamond of the ATR, working in a non-invasive mode. Based on the details acquired using the portable microscope and imaging investigations with UV-induced fluorescence, a few deterioration products were sampled using a scalpel or a swab with absolute ethanol solution and analyzed through FT-IR ATR to better understand the composition of the deteriorated areas. FT-IR ATR spectra were collected using the Nicolet Summit FT-IR spectrometer and the Everest™ Diamond ATR accessory (ThermoFisher Scientific™, Waltham, MA, USA) with a resolution of 8 cm−1 and a laser frequency of 15,798.0 cm−1. 32 scans were performed on each area. The acquired spectra were examined using the instrument library, scientific literature, and the database edited by Vahur et al. [27,28].

3. Results

3.1. Imaging in Visible (VIS) Light and Ultraviolet-Induced Fluorescence (UV)

Images in visible light and UV-induced fluorescence acquired on the different Barbies (front and back) allowed for the identification of the constituent materials. The analysis also enabled the collection of significant information on the Barbies’ state of conservation based on the different fluorescence emissions. The analyzed Barbies showed different fluorescence effects depending on the examined body part (pink, orange, and dark emissions). The main differences can be seen in the legs, arms, and torso (Table 1 and Table 2).
Despite the year of production, the hair of each brunette Barbie exhibits strong absorption of the UV radiation, while the hair of blonde Barbies has different degrees of yellow fluorescence emission based on the color. Only the hair of Barbie #13 shows yellow-greenish emission.
The Barbies #1, 2, 3, and 4 exhibit the typical dim green fluorescence emission of the polyvinyl chloride (PVC) polymer [29]. The Barbie #4 is characterized by the presence of a substance on the torso, showing a white color in visible light (VIS), while a darker fluorescence emission under UV light if compared to the other parts of the body. The crystal-like white exudate is also present on the legs of Barbie #5 and the face of Barbie #6, showing emissions lighter than in the legs and the face, respectively. It is possible to observe a UV radiation-absorbing material on the torso of Barbies #6, 7, 8, 9, 10, 11, and 12, appearing deep dark under UV light compared to the face and limbs, which glow intensively when exposed to UV radiation. In addition, the face and limbs of Barbies #13, 14, and 15 exhibit high absorption of the UV radiation appearing dark if compared to the torsos. Even though the difference cannot be seen under UV light, the faces of Barbies #1, 4, 6, 7, 8, 9, 10, 11, 12, 13, and 14 appear darker if compared with other parts of the body with the same fluorescence emission, due to the presence of an exudate that makes the surface sticky and embedded with dust over time (torso, face, and legs of #1, torso and arms of #4, legs and face of #6, legs of #7, face and legs of #8, limbs of #9, face and legs of #10, limbs of #11, legs of #12, and arms and legs of #13 and #14). Barbies #9, 10, 11, and 13 show differentiated fluorescence emission based on the examined area, even though the difference is not noticeable in VIS light. Indeed, only Barbie #10 exhibits dark-reddish spots—in VIS light—on the upper part of the legs, appearing pink-fluorescent when exposed to UV radiation. On the other hand, it is possible to observe multiple fluorescence effects on Barbies #9, 11, and 12, that do not appear deteriorated in VIS light. Barbies #9 and 11 are characterized by a pinkish fluorescence on the inner and the upper sides of the legs, while strong absorbance of the UV radiation—resulting in a dark appearance—is visible on the remaining parts of the legs, as well as on the torso and arms. This phenomenon is especially evident in Barbie #11, which shows an unevenly spread substance on the arms, appearing deep dark under UV light. In both cases, the face of the doll shows a yellow-greenish fluorescence emission. Barbie #13 exhibits a pinkish fluorescence on the calves and a darker one on the limbs, on which attached fragments of her hair are visible.
The dark-absorbing material that is present on the limbs of most of the Barbies is characterized by different degrees of saturation. This effect could be most likely related to different amounts of plasticizer on the surface. Indeed, migration of the plasticizer is a common deterioration problem in plastics, causing embrittlement of the bulk and adhesion of environmental pollutants and dust on the object’s tacky surface, altering its color and fluorescence emission [22]. In other cases, the differences visible under UV radiation could be related to the constituent polymers, which changed over the years.
The parts of the Barbies exhibiting different fluorescence responses are as follows:
  • The face in Barbies #14 and 15.
  • The limbs in Barbies #5, 7, 9, 11, 12, 13, 14, and 15.
  • The torsos of Barbies #4, 5, 6, 7, 8, 9, 10, 11, and 12.

3.2. Microscopic Observations

Microscopic acquisitions were taken using a 50× magnification to further examine the morphology and the state of conservation of the 15 Barbies (Table 3). The analysis confirms the hypotheses made using multispectral imaging. Faces and legs appear to be the most degraded areas. Indeed, they are often characterized by the presence of an exudate that makes the surface sticky and glossy. This substance is particularly visible on the arms and legs of Barbie #4, but also on the face of Barbie #7—where embedded fibers can be seen—and on the face and limbs of Barbies #8 and #9. Other deterioration phenomena are also better highlighted, such as the white crystal-like substance on the back of Barbie #4, on the legs of Barbie #5, and on the face of Barbie #6. Some of the Barbies also present materials superimposed by the owners, such as the red lipstick on Barbies #1 and 2, scratches induced by scrubbing on Barbie #7, cracking in Barbie #9, and signs of a marker pen ink in Barbies #10, 12, 13, and 15. These alterations of the original doll were not further investigated in this study, as they are considered accidental or intentional damages that cannot be related to intrinsic deterioration phenomena occurring in plastic materials.

3.3. Fourier Transform Infrared Spectroscopy in the Attenuated Total Reflectance Mode (FT-IR ATR)

Spectra were collected examining each element comprising the dolls to characterize their constituent materials and the substances responsible for the evident degradation of the Barbies.
Based on their constituent materials, the Barbies were divided into three groups, namely:
  • Group I: Barbies #1, 2, 3, 4, 5;
  • Group II: Barbies #6, 7, 8, 9, 10, 11, 12;
  • Group III: Barbies #13, 14, 15.
Figure 1 depicts an FT-IR ATR spectrum representative for Group I: the torso, limbs, and face of Barbies of this Group consist of a PVC matrix, which was identified thanks to the characteristic peaks at 1426 cm−1 (CH2–Cl angular deformation), 960 cm−1 (C–H out of plane trans deformation), 831, 691, and 615 cm−1 (C–Cl bond stretching) [30]. A peak at 1640 cm−1 was detected in almost all the spectra acquired on the body of the five Barbies, except for the torso of doll #4 and the legs of #5. This absorption can refer to the presence of carboxylates in the solid products of degradation of PVC and be attributed to the formation of double bonds in the main polymer chain, indicating that some degradation occurred during the crosslinking process of PVC [31]. Spectra acquired on the limbs, torso, and face of the Barbies of Group I—except for the torso of #4—highlighted the presence of the sole plasticizer, identified as a phthalate-based compound for the bands at 1718 cm−1 (phthalate ester), 1450 cm−1 (C–H bending), 1278 cm−1, 1127, and 1027 cm−1 (O–CH2 aromatic group stretching), the small peaks at 1579 cm−1 and 1599 cm−1 (aromatic ring quadrant stretching vibration), and the strong absorbance band at 743 cm−1 (phthalate ortho-substituted aromatic ring) [22,32,33]. It is likely that this can be linked to the presence of a dioctyl phthalate (DOP) or di(2-ethylhexyl) phthalate (DEHP) that have been traditionally used as plasticizers in PVC objects (Figure 1) [34,35,36].
The hair of Barbies belonging to Group I has been identified as polyvinylidene dichloride (PVDC) for the peak at 1405 cm−1 (CH2 bending), the two peaks at 1068 and 1044 cm−1 (C–O stretching vibrations), and the band a 655 cm−1 (C–Cl2 stretching vibrations), while the small peak at 1740 cm−1 corresponding to the C=O stretching is linked to the presence of a plasticizer (Figure 2) [37].
Barbie #4 shows a white crystal-like patina on the torso. The FT-IR ATR analysis detected di(1-butyl)tin(IV) phthalate, highlighting the presence of organotin compounds and plasticizers in the polymeric matrix (Figure 3). Organotin compounds have been commonly used as a thermal stabilizer for PVC compounds even before 1973 due to PVC’s sensitivity to thermal degradation during processing and use [38]. Phthalate-based plasticizers have been also widely added to improve the flexibility, processability, and durability of PVC [39]. Both organotin compounds and plasticizers tend to migrate to the surface of the polymer because they are usually not chemically bonded to the polymer chain [40,41]. Release of the plasticizer is one of the main causes of the deterioration of plasticized PVC, resulting in mass loss, embrittlement of the bulk, and the appearance of sticky exudates on the surface, which could appear as white deposits on the torso of Barbie #4 due to the presence of organotin compounds.
The torso of Barbies from Group II consists of low-density polyethylene (LDPE) matrix (Figure 4). LDPE can be distinguished from high-density polyethylene (HDPE) by the small peak at 1377 cm−1 [42]. The polymer can be also characterized by the peaks at 1467 cm−1 (CH2 bending vibrations), 730 and 717 cm−1 (CH2 rocking vibrations), while the small peak at 1720 cm−1 has to be related to the presence of phthalate plasticizers, even if in smaller amounts than in the PVC parts. The hair of Barbies belonging to Group II again consists of polyvinylidene dichloride (PVDC). Limbs and heads are made of PVC and show the characteristic peaks of the phthalate plasticizer—presumably DEHP or DOP—in the yellow-green-fluorescing areas as well as in the pink-fluorescing ones.
The torso of Barbies from Group III has been characterized as acrylonitrile butadiene styrene (ABS), which explains the yellow-orange fluorescence under UV light compared to the other dolls (Figure 5). ABS’ characteristic peaks can be seen at 1726 cm−1 (C=O stretching), 1583 cm−1 (aromatic stretching vibration), 1492 cm−1 (aromatic C=C bond), 1452 cm−1 (C–H bending), 1070 and 1028 cm−1 (C–O stretching), 965, 910, 758, and 698 cm−1 (C=C bending) [43]. The leg and face of all the Barbies of Group III consist of PVC, while differences can be seen in the spectra collected on the hair and the face. Indeed, while the arms of Barbie #13 are made from PVC, the ones of Barbie #14 show the typical peaks of LDPE.
Furthermore, the spectra acquired from the arms of Barbie #15 can be attributed to ethylene vinyl acetate (EVA) with peaks at 724 cm−1 (CH2 rocking vibrations), 1027 and 1242 cm−1 (C–O stretching), 1380 and 1460 cm−1 (C–H bending), and 1737 cm−1 (C=O stretching) (Figure 6) [44].
Finally, Barbie #14 and 15 again have PVDC hair, whereas Barbie #13 has polypropylene (PP) hair, which is the reason for the green fluorescence emission when irradiated by UV light, as reported in paragraph 3.1 [45]. Characteristic peaks of PP can be observed at 2950, 2920, and 2870 cm−1 (C–H stretching), 1456 cm−1 (C–H bending), 1376 cm−1 (O–H bending), 1166 cm−1 (C=O stretching), 996, 973, 840, and 808 cm−1 (C=C bending) (Figure 7) [46].
A summary of the polymers composing each element of the 15 examined Barbies is reported in Table 4.

4. Discussion

The results obtained by the multi-analytical approach highlighted the frequent use of PVC in Barbies’ manufacturing from 1959 to 1965, which has been gradually replaced by more stable polymers over the years. The characterization of the different plastic elements and degradation products was made possible by using FT-IR ATR spectroscopy, which confirmed the differences in the fluorescence emissions of the plastic elements comprising the 15 Barbies. Indeed, multispectral images in UV light show PVC’s yellowish-green fluorescence emission, while LDPE, which was used to produce the torsos between 1964 and 1974/1976, deeply absorbs the UV radiation, resulting in a dark appearance. Finally, polymers used since 1974/1976—ABS, PP, and EVA—result in yellow-orange, glow-green, and yellow fluorescence emissions, respectively, when irradiated by UV light sources. Barbies showing a grey patina or a pink-reddish fluorescence under UV light—meaning the PVC elements mainly—are the ones that feature the highest inner alteration and the greatest amount of plasticizer on the surface. The presence of phthalate-based plasticizers was evident both in the FT-IR ATR spectra acquired on samples and the ones resulting from the direct analysis of PVC dolls. The doll exhibiting the worst state of conservation is Barbie #11, which has different fluorescence colors on various elements of her body. The FT-IR spectra also confirmed the hypothesis that the main cause of degradation, referring to the glossy exudate and the white crystal-like patina, is the migration of the plasticizers—phthalates—and stabilizers—such as organotin compounds—associated with the polymer processing to improve its flexibility and heat stability.

5. Conclusions and Further Research

This study has provided further information regarding the evolution of the Barbies’ manufacturing process over the years, highlighting changes in the choice of the polymeric matrix for the different body elements. The analytical results were associated with the visible deterioration phenomena that were present on all the Barbies’ surfaces to different degrees. The migration of phthalate-based plasticizers from the bulk up to the surface of the polymer can be considered the main cause of the deterioration of the analyzed dolls. Such a phenomenon results in physical damage to the bulk—embrittlement—and the formation of a tacky patina on the PVC’s outermost layer, which was evident in both VIS and UV light when using the imaging system and portable microscopy.
It was likely for this reason that the Bakelite company carried out an extensive investigations back in 1954 [22,47]. Based on the results from analysis and previous reports, the producers of Barbie dolls had to gradually rethink the chemical composition even before the late 1980s, when a German government law limited the amount of plasticizer allowed in PVC for the safety of children playing with PVC toys [5,23]. Mattel eventually started adapting Barbies’ constituent materials and packaging to the law up to the present day [23]. Over the years, Barbie dolls started to have EVA arms, ABS torsos, heads of a hard vinyl compound, and outer legs in PVC, although using a different formula from the earlier dolls [23]. Even though the evolution process is known to have occurred, only a little information is available regarding the dates on which these structural changes were made. Thus, the present research represents an unprecedented deeper view of the gradual evolution of Barbies’ manufacturing, which enabled assessing the introduction of new polymers—such as LDPE—already used in 1964, and newer ones—such as ABS, PP, and EVA—evident in 1974-1976. Some of these materials are still in use in Mattel’s industry, suggesting that significant changes in the Barbies’ chemical composition occurred already around the ‘70s. Eventually, the implemented multi-analytical approach also allowed for the understanding of polymers’ tendency to deterioration phenomena. Degradation—meaning the migration of the plasticizer and other additives on the outermost surface layer—appears to be more consistent in PVC: the other polymers show plasticizer migration as well, but to a lesser degree.
Nevertheless, given the inner instability of the detected polymeric materials, future research will be devoted to a more in-depth investigation of polymeric fractions, additives, and their degradation products and sub-products (e.g., by micro-invasive analysis by Py-GC-MS or TG-DSC). Then, special attention will be paid to the definition of an appropriate conservation strategy to prevent future deterioration caused by new migration of the additives to the surface. The rapid deterioration of these plastic dolls represents an urgent concern for Cultural Heritage conservation. Hence, innovative preservation approaches need to be improved and tested.

Author Contributions

Conceptualization, A.M.; methodology, A.M.; validation, A.M. and F.C.I.; formal analysis, A.M., M.D., D.T. and C.B.; investigation, A.M., M.D., D.T., C.B. and C.Z.; resources, K.T.C.; data curation, A.M. and C.B.; writing—original draft preparation, A.M. and C.B.; writing—review and editing, A.M., C.B. and F.C.I.; visualization, A.M. and C.B.; supervision, M.F.L.R.; project administration, A.M. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Data Availability Statement

Publicly available datasets were analyzed in this study to compare the acquired FT-IR spectra with already available spectra of standard materials. Data can be found here: https://spectra.chem.ut.ee/ (accessed on 5 September 2022).

Acknowledgments

We would like to express our deepest appreciation to YOCOCU APS’ members, in particular Laura Rivaroli, Lisa Maria Schuberthan, Nicola Pagani, and Alice Hansen, for their help and suggestions to improve this study.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Shashoua, Y. Conservation of Plastics; Routledge: London, UK, 2020. [Google Scholar]
  2. Madden, O.; Learner, T. Preserving Plastics: An Evolving Material, a Maturing profession. In Conservation Perspectives; Getty Conservation Institute: Los Angeles, CA, USA, 2014; pp. 4–9. [Google Scholar]
  3. Thompson, R.C.; Swan, S.H.; Moore, C.J.; Saal, F.S.V. Our plastic age. Philos. Trans. R. Soc. B 2009, 364, 1973–1976. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Kühberger, C. Toys with Historical References as Part of a Material Culture: An Ethnographic Study on Children’s Bedrooms. In Proceedings of the 8th International Toy Research Association World Conference, International Toy Research Association (ITRA), Paris, France, 11–13 July 2018. [Google Scholar]
  5. de Vincentiis, M.; Aversa, R.; Tamburrino, F.; Apicella, A. Analysis of the Barbie Case Study: Social, Material and Technological Evolution Related to the Development of the Products. In Proceedings of the ATINER’s Conference Paper Series, Athens, Greece, 16–19 May 2016. [Google Scholar]
  6. Tulinski, H. Barbie as Cultural Compass: Embodiment, Representation, and Resistance Surrounding the World’s Most Iconized Doll; Sociology Student Scholarship; College of the Holy Cross: Worcester, MA, USA, 2017. [Google Scholar]
  7. Dos Santos Rolim, J. Female Empowerment: A Multimodal Analysis of Representations of Women in Images of Barbie Dolls’ Packages; Universidade Federal da Paraíba: João Pessoa, Brazil, 2020. [Google Scholar]
  8. Gerber, R. Barbie and Ruth: The Story of the World’s Most Famous Doll and the Woman Who Created Her; Harperbusiness: New York, NY, USA, 2010. [Google Scholar]
  9. Esfahani, N.N.; Carrington, V. (Re)scripting Barbie: Postphenomenology and Everyday Artefacts. In Phenomenology of Youth Cultures and Globalization; Routledge: London, UK, 2015; pp. 128–143. [Google Scholar]
  10. Bertrand, L.; Alban, F.; Graham, M. POPART Preservation of Plastic Artefacts in Museum Collections; Comité des Travaux Historiques et Scientifiques—CTHS: Paris, France, 2012. [Google Scholar]
  11. Saldìvar-Guerra, E.; Vivaldo-Lima, E. Handbook of Polymer Synthesis, Characterization, and Processing; John Wiley & Sons, Inc.: Hoboken, NJ, USA, 2013. [Google Scholar]
  12. Moura, J.C.V.P.; Oliveira-Campos, A.M.F.; Griffiths, J. The Effect of Additives on the photostability of Dyed Polymers. Dyes Pigment. 1997, 33, 173–196. [Google Scholar] [CrossRef]
  13. Gardette, J. Fundamental and Technical Aspects of the Photooxidation of Polymers. In Handbook of Polymer Degradation; CRC Press: Boca Raton, FL, USA, 2000. [Google Scholar]
  14. Pino, F.; Fermo, P.; la Russa, M.F.; Ruffolo, S.; Comite, V.; Baghdachi, J.; Pecchioni, E.; Fratini, F.; Cappelletti, G. Advanced mortar coatings for cultural heritage protection. Durability towards prolonged UV and outdoor exposure. Environ. Sci. Pollut. Res. 2017, 24, 12608–12617. [Google Scholar] [CrossRef] [PubMed]
  15. Celina, M.; Ottesen, D.K.; Gillen, K.T.; Clough, R.L. FTIR emission spectroscopy applied to polymer degradation. Polym. Degrad. Stab. 1997, 58, 15–31. [Google Scholar] [CrossRef]
  16. Van Oosten, T. PUR Facts; Amsterdam University Press: Amsterdam, The Netherlands, 2021. [Google Scholar]
  17. Izzo, F.C.; Carrieri, A.; Bartolozzi, G.; van Keulen, H.; Lorenzon, I.; Balliana, E.; Cucci, C.; Grazzi, F.; Picollo, M. Elucidating the composition and the state of conservation of nitrocellulose-based animation cells by means of non-invasive and micro-destructive techniques. J. Cult. Herit. 2019, 35, 254–262. [Google Scholar] [CrossRef]
  18. Izzo, F.C.; van Keulen, H.; Carrieri, A. Assessing the Condition of Complex Poly-Material Artworks by Py-GC-MS: The Study of Cellulose Acetate-Based Animation Cels. Separations 2022, 9, 131. [Google Scholar] [CrossRef]
  19. Feldman, D. Polymer Weathering: Photo-Oxidation. J. Polym. Environ. 2002, 10, 163–173. [Google Scholar] [CrossRef]
  20. Allen, N.S. Photochemistry and Photophysics of Polymer Materials; John Wiley & Sons, Inc.: Hoboken, NJ, USA, 2010. [Google Scholar]
  21. Miller, G.Z.; Harris, Z.E. Hazardous metals in vintage plastic toys measured by a handheld X-ray fluorescence spectrometer. J. Environ. Health 2015, 77, 8–13. [Google Scholar]
  22. Shashoua, Y. Inhibiting the Deterioration of Plasticized Poly (Vinyl Chloride)—A Museum Perspective; Denmark’s Technical University: Kongens Lyngby, Denmark, 2001. [Google Scholar]
  23. Lord, M.G. Forever Barbie: The Unauthorized Biography of a Real Doll; Walker & Company: New York, NY, USA, 2004. [Google Scholar]
  24. Macchia, A.; Biribicchi, C.; Carnazza, P.; Montorsi, S.; Sangiorgi, N.; Demasi, G.; Prestileo, F.; Cerafogli, E.; Colasanti, I.A.; Aureli, H.; et al. Multi-Analytical Investigation of the Oil Painting “Il Venditore di Cerini” by Antonio Mancini and Definition of the Best Green Cleaning Treatment. Sustainability 2022, 14, 3972. [Google Scholar] [CrossRef]
  25. Macchia, A.; Biribicchi, C.; Rivaroli, L.; Aureli, H.; Cerafogli, E.; Colasanti, I.A.; Carnazza, P.; Demasi, G.; La Russa, M.F. Combined Use of Non-Invasive and Micro-Invasive Analytical Investigations to Understand the State of Conservation and the Causes of Degradation of I Tesori del Mare (1901) by Plinio Nomellini. Methods Protoc. 2022, 5, 52. [Google Scholar] [CrossRef]
  26. Macchia, A.; Aureli, H.; Biribicchi, C.; Docci, A.; Alisi, C.; Prestileo, F.; Galiano, F.; Figoli, A.; Mancuso, R.; Gabriele, B.; et al. In Situ Application of Anti-Fouling Solutions on a Mosaic of the Archaeological Park of Ostia Antica. Materials 2022, 15, 5671. [Google Scholar] [CrossRef]
  27. Database of ATR-FT-IR Spectra of Various Materials. Available online: https://spectra.chem.ut.ee/ (accessed on 5 August 2019).
  28. Vahur, S.; Teearu, A.; Peets, P.; Joosu, L.; Leito, I. ATR-FT-IR spectral collection of conservation materials in the extende region of 4000-80 cm−1. Anal. Bioanal. Chem. 2016, 408, 3373–3379. [Google Scholar] [CrossRef]
  29. Munoz, L.P.; Baez, A.G.; McKinney, D.; Garelick, H. Characterisation of “flushable” and “non-flushable” commercial wet wipes using microRaman, FTIR spectroscopy and fluorescence microscopy: To flush or not to flush. Environ. Sci. Pollut. Res. 2018, 25, 20268–20279. [Google Scholar] [CrossRef] [PubMed]
  30. Chen, J.; Nie, X.A.; Jiang, J.C.; Zhou, Y.H. Thermal degradation and plasticizing mechanism of poly(vinyl chloride) plasticized with a novel carnadol derived plasticizer. IOP Conf. Ser. Mater. Sci. Eng. 2017, 292, 012008. [Google Scholar] [CrossRef]
  31. Zaikov, G.E.; Jimenez, A. Polymer Analysis, Degradation and Stabilization; Nova Science Pub Inc.: New York, NY, USA, 2005. [Google Scholar]
  32. Andjelković, T.; Bogdanović, D.; Kostić, I.; Kocić, G.; Nikolić, G.; Pavlović, R. Phthalates leaching from plastic food and pharmaceutical contact materials by FTIR and GC-MS. Environ. Sci. Pollut. Res. 2021, 28, 31380–31390. [Google Scholar] [CrossRef] [PubMed]
  33. Hankett, J.M.; Welle, A.; Lahann, J.; Chen, Z. Evaluating UV/H2O2 Exposure as a DEHP Degradation Treatment for Plasticized PVC. J. Appl. Polym. Sci. 2014, 131, 40649. [Google Scholar] [CrossRef] [Green Version]
  34. Erythropel, H.C.; Maric, M.; Nicell, J.A.; Leask, R.L.; Yargeau, V. Leaching of the plasticizer di(2-ethylhexyl)phthalate (DEHP) from plastic containers and the question of human exposure. Appl. Microbiol. Biotechnol. 2014, 98, 9967–9981. [Google Scholar] [CrossRef]
  35. Navarro, R.; Perez Perrino, M.; Gomez Tardajos, M.; Reinecke, H. Phthalate Plasticizers Covalently Bound to PVC: Plasticization with Suppressed Migration. Macromolecules 2010, 43, 2377–2381. [Google Scholar] [CrossRef]
  36. Demir, A.P.T.; Ulutan, S. Migration of Phthalate and Non-Phthalate Plasticizers Out of Plasticized PVC Films into Air. J. Appl. Polym. Sci. 2012, 128, 1948–1961. [Google Scholar]
  37. Peltzer, M.A.; Simoneau, C. Report of an Interlaboratory Comparison from the European Reference Laboratory for Food Contact Materials; Publications Office of the European Union: Luxembourg, 2013. [Google Scholar]
  38. Piver, W.T. Organotin Compounds: Industrial Applications and Biological Investigation. Environ. Health Perspect. 1973, 4, 61–79. [Google Scholar] [CrossRef]
  39. Kim, D.Y.; Chun, S.; Mohamed, D.F.M.S.; Kim, H.; Kang, D.; An, J.; Park, S.; Kwon, H.; Kwon, J. Phthalate Plasticizers in Children’s Products and Estimation of Exposure: Importance of Migration Rate. Int. J. Environ. Res. Public Health 2020, 17, 8582. [Google Scholar] [CrossRef] [PubMed]
  40. Adams, W.A.; Xu, Y.; Little, J.C.; Fristachi, A.F.; Rice, G.E.; Impellitteri, C.A. Predicting the Migration Rate of Dialkyl Organotins from PVC Pipe into Water. Environ. Sci. Technol. 2011, 45, 6902–6907. [Google Scholar] [CrossRef]
  41. Mandrile, L.; Vona, M.; Giovannozzi, A.M.; Salafranca, J.; Martra, G.; Rossi, A.M. Migration study of organotin compounds from food packaging by surface-enhanced Raman scattering. Talanta 2020, 220, 121408. [Google Scholar] [CrossRef] [PubMed]
  42. Jung, M.R.; Horgen, F.D.; Orski, S.V.; Rodriguez, V.; Beers, K.L.; Balazs, G.H.; Jones, T.T.; Work, T.M.; Brignac, K.C.; Royer, S.J.; et al. Validation of ATR FT-IR to identify polymers of plastic marine debris, including those ingested by marine organisms. Mar. Pollut. Bull. 2018, 127, 704–716. [Google Scholar] [CrossRef] [PubMed]
  43. Puype, F.; Samsonek, J.; Knoop, J.; Egelkraut-Holtus, M.; Ortlieb, M. Evidence of waste electrical and electronic equipment (WEEE) relevant substances in polymeric food-contact articles sold on the European market. Food Addit. Contam. Part A 2015, 32, 410–426. [Google Scholar] [CrossRef]
  44. Quang, T.D.; Trang, N.T.T.; Chinh, N.T.; Nguyen, G.; Lam, T.D.; Hoang, T. Sustainable composite materials based on ethylene-vinylacetate copolymer and organo-modified silica. Green Processing Synth. 2016, 5, 557–566. [Google Scholar]
  45. Poszwa, P.; Kędzierski, K.; Barszcz, B.; Nowicka, A.B. Fluorescence confocal microscopy as effective testing method of polypropylene fibers and single polymer composites. Polym. Test. 2016, 53, 174–179. [Google Scholar] [CrossRef]
  46. Fang, J.; Zhang, L.; Sutton, D.; Wang, X.; Lin, T. Needleless Melt-Electrospinning of Polypropylene Nanofibres. J. Nanomater. 2012, 2012, 1–9. [Google Scholar] [CrossRef] [Green Version]
  47. Quackenbos, H.M. Plasticizers in vinyl chloride resins. Ind. Eng. Chem. 1954, 46, 1335–1341. [Google Scholar] [CrossRef]
Figure 1. FT-IR ATR spectrum collected on the arm of Barbie #1 and shown as a model spectrum of PVC elements in all the other dolls, with the reference spectra of PVC and n-octyl n-decyl phthalate (plasticizer).
Figure 1. FT-IR ATR spectrum collected on the arm of Barbie #1 and shown as a model spectrum of PVC elements in all the other dolls, with the reference spectra of PVC and n-octyl n-decyl phthalate (plasticizer).
Polymers 14 04287 g001
Figure 2. FT-IR ATR spectrum collected on the hair of Barbie #2 and shown as a model spectrum of PVDC hair in all the other dolls, with the reference spectrum of PVDC.
Figure 2. FT-IR ATR spectrum collected on the hair of Barbie #2 and shown as a model spectrum of PVDC hair in all the other dolls, with the reference spectrum of PVDC.
Polymers 14 04287 g002
Figure 3. FT-IR ATR spectrum collected on the crystal-like white patina on the torso of Barbie #4, with the reference spectrum of a phthalate-organotin compound.
Figure 3. FT-IR ATR spectrum collected on the crystal-like white patina on the torso of Barbie #4, with the reference spectrum of a phthalate-organotin compound.
Polymers 14 04287 g003
Figure 4. FT-IR ATR spectrum collected on the torso of Barbie #6 and shown as a model spectrum of LDPE elements in all the other dolls, with the reference spectrum of LDPE.
Figure 4. FT-IR ATR spectrum collected on the torso of Barbie #6 and shown as a model spectrum of LDPE elements in all the other dolls, with the reference spectrum of LDPE.
Polymers 14 04287 g004
Figure 5. FT-IR ATR spectrum collected on the torso of Barbie #13 and shown as a model spectrum of ABS elements in all the other dolls, with the reference spectrum of ABS.
Figure 5. FT-IR ATR spectrum collected on the torso of Barbie #13 and shown as a model spectrum of ABS elements in all the other dolls, with the reference spectrum of ABS.
Polymers 14 04287 g005
Figure 6. FT-IR ATR spectrum collected on the arm of Barbie #15 with the reference spectrum of EVA.
Figure 6. FT-IR ATR spectrum collected on the arm of Barbie #15 with the reference spectrum of EVA.
Polymers 14 04287 g006
Figure 7. FT-IR ATR spectrum collected on the hair of Barbie #13 with the reference spectrum of PP.
Figure 7. FT-IR ATR spectrum collected on the hair of Barbie #13 with the reference spectrum of PP.
Polymers 14 04287 g007
Table 1. Multispectral images (VIS and UV) of the 15 Barbies including a VIS/UV reference standard: right side.
Table 1. Multispectral images (VIS and UV) of the 15 Barbies including a VIS/UV reference standard: right side.
Barbie #1 (1959/60)Barbie #2 (1959/60)Barbie #3 (1964)
VISUVVISUVVISUV
Polymers 14 04287 i001Polymers 14 04287 i002Polymers 14 04287 i003Polymers 14 04287 i004Polymers 14 04287 i005Polymers 14 04287 i006
Barbie #4 (1964)Barbie #5 (1964)Barbie #6 (1964)
VISUVVISUVVISUV
Polymers 14 04287 i007Polymers 14 04287 i008Polymers 14 04287 i009Polymers 14 04287 i010Polymers 14 04287 i011Polymers 14 04287 i012
Barbie #7 (1965)Barbie #8 (1965)Barbie #9 (1972)
VISUVVISUVVISUV
Polymers 14 04287 i013Polymers 14 04287 i014Polymers 14 04287 i015Polymers 14 04287 i016Polymers 14 04287 i017Polymers 14 04287 i018
Barbie #10 (1972)Barbie #11 (1974/76)Barbie #12 (1974/76)
VISUVVISUVVISUV
Polymers 14 04287 i019Polymers 14 04287 i020Polymers 14 04287 i021Polymers 14 04287 i022Polymers 14 04287 i023Polymers 14 04287 i024
Barbie #13 (1974/76)Barbie #14 (1974/76)Barbie #15 (1974/76)
VISUVVISUVVISUV
Polymers 14 04287 i025Polymers 14 04287 i026Polymers 14 04287 i027Polymers 14 04287 i028Polymers 14 04287 i029Polymers 14 04287 i030
Table 2. Multispectral images (VIS and UV) of the 15 Barbies including a VIS/UV reference standard: backside.
Table 2. Multispectral images (VIS and UV) of the 15 Barbies including a VIS/UV reference standard: backside.
Barbie #1 (1959/60)Barbie #2 (1959/60)Barbie #3 (1964)
VISUVVISUVVISUV
Polymers 14 04287 i031Polymers 14 04287 i032Polymers 14 04287 i033Polymers 14 04287 i034Polymers 14 04287 i035Polymers 14 04287 i036
Barbie #4 (1964)Barbie #5 (1964)Barbie #6 (1964)
VISUVVISUVVISUV
Polymers 14 04287 i037Polymers 14 04287 i038Polymers 14 04287 i039Polymers 14 04287 i040Polymers 14 04287 i041Polymers 14 04287 i042
Barbie #7 (1965)Barbie #8 (1965)Barbie #9 (1972)
VISUVVISUVVISUV
Polymers 14 04287 i043Polymers 14 04287 i044Polymers 14 04287 i045Polymers 14 04287 i046Polymers 14 04287 i047Polymers 14 04287 i048
Barbie #10 (1972)Barbie #11 (1974/76)Barbie #12 (1974/76)
VISUVVISUVVISUV
Polymers 14 04287 i049Polymers 14 04287 i050Polymers 14 04287 i051Polymers 14 04287 i052Polymers 14 04287 i053Polymers 14 04287 i054
Barbie #13 (1974/76)Barbie #14 (1974/76)Barbie #15 (1974/76)
VISUVVISUVVISUV
Polymers 14 04287 i055Polymers 14 04287 i056Polymers 14 04287 i057Polymers 14 04287 i058Polymers 14 04287 i059Polymers 14 04287 i060
Table 3. Microscopic images (magnification: 50×) under VIS and UV light: details of the head, torso, legs, arms, and back on each Barbie identified through the ID number.
Table 3. Microscopic images (magnification: 50×) under VIS and UV light: details of the head, torso, legs, arms, and back on each Barbie identified through the ID number.
IDHeadTorsoLegsArmsBack
1Polymers 14 04287 i061Polymers 14 04287 i062Polymers 14 04287 i063Polymers 14 04287 i064Polymers 14 04287 i065Polymers 14 04287 i066Polymers 14 04287 i067Polymers 14 04287 i068Polymers 14 04287 i069Polymers 14 04287 i070
2NANAPolymers 14 04287 i071Polymers 14 04287 i072Polymers 14 04287 i073Polymers 14 04287 i074Polymers 14 04287 i075Polymers 14 04287 i076Polymers 14 04287 i077Polymers 14 04287 i078
3Polymers 14 04287 i079Polymers 14 04287 i080Polymers 14 04287 i081Polymers 14 04287 i082Polymers 14 04287 i083Polymers 14 04287 i084Polymers 14 04287 i085Polymers 14 04287 i086Polymers 14 04287 i087Polymers 14 04287 i088
4Polymers 14 04287 i089Polymers 14 04287 i090Polymers 14 04287 i091Polymers 14 04287 i092Polymers 14 04287 i093Polymers 14 04287 i094Polymers 14 04287 i095Polymers 14 04287 i096Polymers 14 04287 i097Polymers 14 04287 i098
5Polymers 14 04287 i099Polymers 14 04287 i100Polymers 14 04287 i101Polymers 14 04287 i102Polymers 14 04287 i103Polymers 14 04287 i104Polymers 14 04287 i105Polymers 14 04287 i106Polymers 14 04287 i107Polymers 14 04287 i108
6Polymers 14 04287 i109Polymers 14 04287 i110Polymers 14 04287 i111Polymers 14 04287 i112Polymers 14 04287 i113Polymers 14 04287 i114Polymers 14 04287 i115Polymers 14 04287 i116Polymers 14 04287 i117Polymers 14 04287 i118
7Polymers 14 04287 i119Polymers 14 04287 i120Polymers 14 04287 i121Polymers 14 04287 i122Polymers 14 04287 i123Polymers 14 04287 i124Polymers 14 04287 i125Polymers 14 04287 i126Polymers 14 04287 i127Polymers 14 04287 i128
8Polymers 14 04287 i129Polymers 14 04287 i130Polymers 14 04287 i131Polymers 14 04287 i132Polymers 14 04287 i133Polymers 14 04287 i134Polymers 14 04287 i135Polymers 14 04287 i136Polymers 14 04287 i137Polymers 14 04287 i138
9Polymers 14 04287 i139Polymers 14 04287 i140Polymers 14 04287 i141Polymers 14 04287 i142Polymers 14 04287 i143Polymers 14 04287 i144Polymers 14 04287 i145Polymers 14 04287 i146Polymers 14 04287 i147Polymers 14 04287 i148
10Polymers 14 04287 i149Polymers 14 04287 i150Polymers 14 04287 i151Polymers 14 04287 i152Polymers 14 04287 i153Polymers 14 04287 i154Polymers 14 04287 i155Polymers 14 04287 i156Polymers 14 04287 i157Polymers 14 04287 i158
11Polymers 14 04287 i159Polymers 14 04287 i160Polymers 14 04287 i161Polymers 14 04287 i162Polymers 14 04287 i163Polymers 14 04287 i164Polymers 14 04287 i165Polymers 14 04287 i166Polymers 14 04287 i167Polymers 14 04287 i168
12Polymers 14 04287 i169Polymers 14 04287 i170Polymers 14 04287 i171Polymers 14 04287 i172Polymers 14 04287 i173Polymers 14 04287 i174Polymers 14 04287 i175Polymers 14 04287 i176Polymers 14 04287 i177Polymers 14 04287 i178
13Polymers 14 04287 i179Polymers 14 04287 i180Polymers 14 04287 i181Polymers 14 04287 i182Polymers 14 04287 i183Polymers 14 04287 i184Polymers 14 04287 i185Polymers 14 04287 i186Polymers 14 04287 i187Polymers 14 04287 i188
14Polymers 14 04287 i189Polymers 14 04287 i190Polymers 14 04287 i191Polymers 14 04287 i192Polymers 14 04287 i193Polymers 14 04287 i194Polymers 14 04287 i195Polymers 14 04287 i196Polymers 14 04287 i197Polymers 14 04287 i198
15Polymers 14 04287 i199Polymers 14 04287 i200Polymers 14 04287 i201Polymers 14 04287 i202Polymers 14 04287 i203Polymers 14 04287 i204Polymers 14 04287 i205Polymers 14 04287 i206Polymers 14 04287 i207Polymers 14 04287 i208
Table 4. Results of the FT-IR ATR analysis, based on the characteristic peaks of the Barbies’ constituent materials.
Table 4. Results of the FT-IR ATR analysis, based on the characteristic peaks of the Barbies’ constituent materials.
IDYearTorsoArmsLegsFaceHair
11959/1960PVCPVCPVCPVCPVDC
21959/1960PVCPVCPVCPVCPVDC
31964PVCPVCPVCPVCPVDC
41964PVCPVCPVCPVCPVDC
51964PVCPVCPVCPVCPVDC
61964LDPEPVCPVCPVCPVDC
71965LDPEPVCPVCPVCPVDC
81965LDPEPVCPVCPVCPVDC
91972LDPEPVCPVCPVCPVDC
101972LDPEPVCPVCPVCPVDC
111974/1976LDPEPVCPVCPVCPVDC
121974/1976LDPEPVCPVCPVCPVDC
131974/1976ABSPVCPVCPVCPP
141974/1976ABSLDPEPVCPVCPVDC
151974/1976ABSPEVAPVCPVCPVDC
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Macchia, A.; Biribicchi, C.; Zaratti, C.; Testa Chiari, K.; D’Ambrosio, M.; Toscano, D.; Izzo, F.C.; La Russa, M.F. Mattel’s Barbie: Investigation of a Symbol—Analysis of Polymeric Matrices and Degradation Phenomena for Sixteen Dolls from 1959 to 1976. Polymers 2022, 14, 4287. https://doi.org/10.3390/polym14204287

AMA Style

Macchia A, Biribicchi C, Zaratti C, Testa Chiari K, D’Ambrosio M, Toscano D, Izzo FC, La Russa MF. Mattel’s Barbie: Investigation of a Symbol—Analysis of Polymeric Matrices and Degradation Phenomena for Sixteen Dolls from 1959 to 1976. Polymers. 2022; 14(20):4287. https://doi.org/10.3390/polym14204287

Chicago/Turabian Style

Macchia, Andrea, Chiara Biribicchi, Camilla Zaratti, Katiuscia Testa Chiari, Martina D’Ambrosio, Denise Toscano, Francesca Caterina Izzo, and Mauro Francesco La Russa. 2022. "Mattel’s Barbie: Investigation of a Symbol—Analysis of Polymeric Matrices and Degradation Phenomena for Sixteen Dolls from 1959 to 1976" Polymers 14, no. 20: 4287. https://doi.org/10.3390/polym14204287

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.